It is used especially in machinery of the food industry, his tenacity is a very important property, however, the resistance is not too high. Application: surgical instrumentation implements, links for chain, pins, bushings, common fasteners and staples.

Low carbon steel with easy machining, re-sulfurized and reflowed. It is used in the manufacture of parts of low and medium mechanical requirements with the maximum machinability index. Lead improves the surface finish, also acts as a lubricant helping to prevent tool wear and serving as chip fragilizer. Applications: manufacture of screws, couplings, bushings, and in general in the manufacture of parts in large series.

It is an alloy carbon steel, used in the manufacture of pieces of medium section and small where high efforts of fatigue and torsion are required. It is supplied calibrated or turning  in the bonus state (tempered y revenido con una dureza de suministro de 28 a 32 HRC) Applications: parts for the automotive industry, parts for machinery, forged parts, oil industry, 8 grade high strength fasteners.

Low carbon steel, It is especially used in machinery where tenacity it is an important property, however, the resistance is not too high. Application: parts that do not have high mechanical requirements as axes, grade 2 fasteners, chain links, pins, Bushings, current fasteners and staples. Supplied with black finish, calibrated and turned, with a hardness of 180 HB.

Medium carbon steel susceptible to heat treatment, with cooling in oil. Its content of carbon and manganese it gives a greater depth of hardening. Applications: medium strength parts in the automotive industry, forged and stamped parts, shafts, pieces of weapons, screws grade 5, manufacture of tools.

They are manufactured under the norm SAE 1518 Carbon-manganese steel, which has good characteristics for cementation, it is easily machined and has good weldability due to its chemical composition.

Applications: pinions, bushes, bolts, spacers, shirts, rollers of various types. In general it is used for parts with interior perforations, with wide application in the automotive and general industry for manufacturing parts subjected to wear and abrasion.

It is available in diameters from 32 x 250 x 200mm until 16 of outer and inner diameter.